1. For Direct Composite Restorations
and
2. For Composite Core Build-Ups:
1. Etch the preparation for 15 seconds
using UNI-ETCH®*
w/ BAC and rinse thoroughly. Remove excess water using
a foam pellet, leaving the preparation visibly moist.
2. Dispense an equal number of drops
of ALL-BOND 3 Parts A and B (1:1) into
a mixing well. Using a brush, mix well for 5 seconds.
3. Apply 1-2 coats onto the tooth preparation.
4. Gently but thoroughly air dry until
there is no visible movement of the material. The surface
should appear shiny; otherwise, apply additional coats
of ALL-BOND 3 and repeat Step 4.
5. Light cure for 10 seconds at 500mW/cm2.
6. Apply one thin coat of ALL-BOND
3 RESIN. Air thin if necessary.
7. Light cure for 10 seconds at 500mW/cm2.
8. Continue with placement of restorative
material.
3. For Desensitization of Crown Preparations
Prior to Impression Making/Provisionalization:
1. Follow steps 1-7 on previous page,
then remove the oxygen-inhibited layer with an alcohol-moistened
cotton pellet or 2x2 gauze and make the impression.
2. Continue with temporization procedure.
It is recommended to coat the preparation with a water-based
lubricant leaving 1-2mm at the margins for adhesion
of the temporary cement.
4. For Indirect
Restorations (Composite, Metal, Porcelain)
Tooth Preparation:
1. Etch the preparation using UNI-ETCH w/ BAC for 15
seconds and rinse thoroughly. Remove excess water using
a foam pellet, leaving the preparation visibly moist.
2. Dispense an equal number of drops
of ALL-BOND 3 Parts A and B (1:1) into
a mixing well. Using a brush, mix well for 5 seconds.
3. Apply 1-2 coats onto the tooth preparation.
4. Gently but thoroughly air dry until
there is no visible movement of the material. The surface
should appear shiny; otherwise, apply additional coats
of ALL-BOND 3 and repeat Step 4.
5. Light cure for 10 seconds at 500mW/cm2.
NOTE: It is not necessary to use ALL-BOND
3 RESIN.
6. Continue with cementation procedure.
Indirect Restoration Preparation:
For metal or composite indirect restorations:
1. Prepare the internal surface of the restoration according
to instructions provided by the laboratory.
2. Dispense an equal number of drops
of ALL-BOND 3 Parts A and B (1:1) into
a mixing well. Using a brush, mix well for 5 seconds.
3. Apply 1-2 coats to the internal surface
of the restoration.
4. Gently but thoroughly air dry until
there is no visible movement of the material. The surface
should appear shiny; otherwise, apply additional coats
of ALL-BOND 3 and repeat Step 4.
5. Light cure for 10 seconds at 500mW/cm2.
For all-ceramic restorations:
IMPORTANT: Since different ceramics
require different surface treatments, contact laboratory
for proper internal surface treatment instructions.
1. If the laboratory recommends silanation,
apply 1-2 thin coats of silane, such as BIS-SILANE™*,
to the internal surface and wait for 30 seconds. Dry
with air syringe.
NOTE: Surface of the porcelain will
not look any different than prior to BIS-SILANE application.
2a. For All-Ceramic Restorations Except Veneers:
Dispense an equal number of drops of ALL-BOND
3 Parts A and B (1:1) into a mixing well. Using
a brush, mix well for 5 seconds. Apply 1-2 coats to
the internal surface of the restoration.
b. For Veneers: Apply
1-2 coats of PORCELAIN BONDING RESIN* instead of ALL-BOND
3 Parts A and B to the internal surface of
the restoration to maintain long-term shade stability.
Do NOT light cure. Skip Steps 3 and 4.
3. Gently but thoroughly air dry until
there is no visible movement of the material. The surface
should appear shiny; otherwise, apply additional coats
of ALL-BOND 3 and repeat Step 3.
4. Light cure for 10 seconds at 500mW/cm2.
5. For Endodontic
Post Bonding:
1. Prepare post space according to manufacturer’s
instructions. If a metal post is used, prepare the surface
of the post per manufacturer’s instructions.
2. Etch the canal using UNI-ETCH w/
BAC for 15 seconds. Rinse thoroughly and remove excess
water with a brief burst of air or a paper point to
remove any pooled water from the canal.
3. Dispense an equal number of drops
of ALL-BOND 3 Parts A and B (1:1) into
a mixing well. Using a brush, mix well for 5 seconds.
With an endodontic brush, apply 1 coat of ALL-BOND
3 Parts A and B into the canal. Remove excess
pooling of material with paper points or light suction.
Follow with a gentle stream of air to thoroughly air
dry. Light-curing is not necessary due to the dual-cure
capability of ALL-BOND 3.
NOTE: The paper point step is important
for removal of any pooled adhesive so that there is
no interference in complete seating of the post.
4. Apply one layer of ALL-BOND
3 Parts A and B to the post and gently air
dry. Light cure for 10 seconds at 500mW/cm2.
Proceed with post cementation per manufacturer’s
instructions.
6. For Porcelain
Repair:
1. Isolate the area to be repaired with a rubber dam.
2. It is best to prepare the porcelain using a long
bevel.
3. Sandblast exposed metal and/or surrounding porcelain
to be repaired for 1-2 seconds. An alternative to sandblasting
is to abrade surfaces with a coarse diamond bur. Rinse
with water and air dry.
4. BARRIER GEL* may be placed to
protect soft tissue and other areas where etching is
not desired.
| WARNING: There
are several PRECAUTIONS that must
be adhered to when working with PORCELAIN ETCHANT.
DO NOT use PORCELAIN ETCHANT until
you have read and understood the instructions
that pertain to that product: 4% or 9.5%
PORCELAIN ETCHANT Instructions For Use. |
5. Apply BISCO’s
PORCELAIN ETCHANT*
to the dried repair site and allow to dwell for 5-6
minutes for 4% PORCELAIN ETCHANT and 1-2 minutes for
9.5% PORCELAIN ETCHANT. To evacuate hydrofluoric acid
vapors, hold evacuator tip adjacent to repair site.
Monitor the etch site throughout the entire procedure.
CAUTION: Prior to intraoral use,
confirm that PORCELAIN ETCHANT syringe tip is adequately
placed and tightly attached. Test the etchant to confirm
that it is flowing freely from the syringe tip by expressing
a small amount onto a mixing pad. If there is resistance
to flow, DO NOT proceed. Replace tip and test flow again
before using on patient.
NOTE: Not all ceramic systems are etchable
and etching times may vary with various ceramic materials.
6. Apply high-speed suction to remove
the PORCELAIN ETCHANT. Rinse with copious amounts of
water and air dry. The etched surface should appear
dull and frosty.
7. Apply 1-2 thin coats of silane such
as BIS-SILANE to the etched porcelain surface and allow
it to dwell for 30 seconds. Air dry to evaporate the
solvent.
8. Dispense an equal number of drops
of ALL-BOND 3 Parts A and B (1:1) into
a mixing well. Using a brush, mix well for 5 seconds.
Apply 1-2 coats to the metal and porcelain surfaces.
Gently air dry to evaporate the solvent. Light cure
for 10 seconds at 500mW/cm2.
9. If metal is visible, apply DUAL-CURED
OPAQUER*: Shake bottles and mix base and catalyst (1:1)
in a mixing well. Apply a thin layer to mask the metal.
Light cure for 30 seconds at 500mW/cm2.
10. Proceed with composite layering
and finishing. The preferred composite should be a hybrid
or nano-hybrid such as AELITE™* ALL-PURPOSE BODY.
Pure microfilled or nanofilled composites are not recommended
for porcelain repair due to low impact strengths.
7. For Composite
Repair:
1. Remove layer of old composite and
bevel enamel margin, if present.
2. Etch the preparation using UNI-ETCH
w/ BAC for 15 seconds, rinse thoroughly and air dry.
If dentin is present, leave the dentin visibly moist.
3. Dispense an equal number of drops
of ALL-BOND 3 Parts A and B (1:1) into
a mixing well. Using a brush, mix well for 5 seconds.
4. Apply 1-2 coats onto the composite
and tooth structure.
5. Gently but thoroughly air dry until
there is no visible movement of the material. The surface
should appear shiny; otherwise, apply additional coats
of ALL-BOND 3 and repeat Step 5.
6. Light cure for 10 seconds at 500mW/cm2.
7. Proceed with composite layering and
finishing.
8. For Composite to Metal / Set Amalgam (Direct
Metal/Alloy Veneering):
1. Prepare metal surface per manufacturer’s
instructions. Rinse with water and air dry.
2. If tooth structure is present, etch
with UNI-ETCH w/ BAC for 15 seconds and rinse thoroughly.
Remove excess water using a foam pellet, leaving the
preparation visibly moist.
3. Dispense an equal number of drops
of ALL-BOND 3 Parts A and B into a
mixing well. Using a brush, mix well for 5 seconds.
4. Apply 1-2 coats onto the metal and
tooth structure.
5. Gently but thoroughly air dry until
there is no visible movement of the material. The surface
should appear shiny; otherwise, apply additional coats
of ALL-BOND 3 and repeat Step 5.
6. Light cure for 10 seconds at 500mW/cm2.
7. Apply DUAL-CURED OPAQUER: Shake bottles
and mix base and catalyst (1:1) in a mixing well. Apply
a thin layer to mask metal. Light cure for 30 seconds
at 500mW/cm2.
8. Proceed with composite layering and
finishing.
9. For Exposed
Root Desensitization:
1. Etch the dentin using UNI-ETCH w/ BAC for 15 seconds
and rinse thoroughly. Remove excess water using a foam
pellet, leaving the preparation visibly moist.
2. Dispense an equal number of drops
of ALL-BOND 3 Parts A and B into a
mixing well. Using a brush, mix well for 5 seconds.
3. Apply 1-2 coats onto the tooth preparation.
4. Gently but thoroughly air dry until
there is no visible movement of the material. The surface
should appear shiny; otherwise, apply additional coats
of ALL-BOND 3 and repeat Step 4.
5. Light cure for 10 seconds at 500mW/cm2.
6. Apply a thin coat of ALL-BOND
3 RESIN. Air thin if necessary.
7. Light cure for 10 seconds at 500mW/cm2.
8. Remove the oxygen-inhibited layer
with an alcohol-moistened cotton pellet or 2x2 gauze.
STORAGE: Store
at room temperature (22°C/72°F). Refer to individual
component labels for specific expiration dates.
PRECAUTIONS: Unpolymerized resins may
cause skin sensitization in susceptible persons. In
case of contact with the skin, wash thoroughly with
soap and water.
WARRANTY: BISCO, Inc. recognizes its
responsibility to replace products if proven to be defective.
BISCO, Inc. does not accept liability for any damages
or loss, either direct or consequential, stemming from
the use of or inability to use the products as described.
Before using, it is the responsibility of the user to
determine the suitability of the product for its intended
use. The user assumes all risk and liability in connection
therewith.
CAUTION: U.S. Federal law restricts
this device to sale by or on the order of a dental professional.
*
ALL-BOND 2 and UNI-ETCH are registered trademarks of
BISCO, Inc.
ALL-BOND 3, BIS-SILANE and AELITE are trademarks of
BISCO, Inc.
PORCELAIN BONDING RESIN, BARRIER GEL, PORCELAIN ETCHANT
and DUAL-CURED OPAQUER are manufactured by BISCO, Inc.
BISCO, Inc.
1100 W. Irving Park Rd.
Schaumburg, IL 60193
1-800-BIS-DENT
847-534-6000
www.bisco.com
CE ADMINISTRATOR
Bisico France -
Mr. Fred Picavet
L'Opera- BP. 60
13680 Lançon De Provence
France
Phone: 33-490-42-9292
Fax: 33-490-42-9261
Licensed under 1 or more of the following U.S. Patents:
5,789,610, 5,270,351 & 5,401,783.
See also U.S. Patent 5,348,988.
Patent Pending
IN-159
Rev. 3/07
|