BIS-CORE™*
Core Build-Up Composite
INSTRUCTIONS FOR USE |
|
BIS-CORE is a dual-cured, highly filled, radiopaque core build-up composite. The high viscosity BASE PASTE is a universal dentin shade and may be used alone as a light-cured CORE build-up material. When the BASE PASTE is mixed with the CATALYST PASTE, the resultant mixture is a dual-cured, low viscosity composite ideal for intracoronal syringe placement. The dual-cured CATALYST PASTE is available in two shades, Natural and Opaque. BIS-CORE has superior physical properties with a compressive strength greater than 40,000 psi resulting in a strong, easy-to-use core build-up material. BIS-CORE is intended for use with an adhesive
system such as ALL-BOND 2®*, ALL-BOND 3®*, ONE-STEP®* /ONE-STEP PLUS or ALL-BOND SE ®*. |
| TECHNICAL
INFORMATION |
At room temperature (20°C/68°F - 25°C/77°F) |
Working
Time:
Setting Time: |
Minimum 1 min. 30 sec.
Minimum 5 min. 30 sec. |
| Working and setting time will be accelerated in the warm intraoral environment. Also, the cement will set quickly once it comes in contact with ALL-BOND 2 primers on the tooth. |
INSTRUCTIONS FOR USE |
CORE
BUILD-UP
1. If a post is indicated, cement post into post preparation according to manufacturer's instructions.
2. If using a total-etch adhesive, etch remaining coronal tooth structure with an etchant such as UNI-ETCH®* w/BAC according to manufacturer's instructions.
OR if using a self-etch adhesive, skip this step and proceed to step 3. |
| 3. Apply an adhesive such as ALL-BOND 2, ALL-BOND 3, ONE-STEP/
ONE-STEP PLUS or ALL-BOND SE according to manufacturer's instructions. |
Refer to manufacturer’s instructions. Unlike ALL-BOND SE and ONE-STEP/ONE-STEP PLUS, not all self-etch or total etch one-bottle adhesives bond to dual-cured or self-cured composites. |
4. For Dual-Cured Method: |
a) The ratio of BASE PASTE to CATALYST PASTE may be varied to alter the
setting time.
• To shorten the setting time: Increase amount of BASE PASTE
• To lengthen the setting time: Increase amount of CATALYST PASTE
b) Dispense desired amount of BIS-CORE BASE and CATALYST PASTES onto a light-protected mixing pad by turning syringe handle clockwise. To prevent excess material escaping from syringe, turn handle COUNTERCLOCKWISE immediately after the desired amount is dispensed. Mix to a uniform paste (10-15 seconds).
c) Place directly into preparation or fill a High Viscosity Unit-Dose Tip with the composite and inject into the preparation and around the post, if present. Continue to build until cavity preparation is filled to the desired level.
d) Light cure for 20 seconds per surface or allow the material to self cure, and continue with preparation.
|
5. For Light-Cured Method: |
a) Dispense desired amount of BIS-CORE BASE PASTE onto a light-protected mixing pad by turning syringe handle clockwise. To prevent excess material escaping from syringe, turn handle counterclockwise immediately after the desired amount is dispensed.
b) Place directly into preparation or fill a High Viscosity Unit-Dose Tip
with the composite and inject into the preparation and around the post,
if present. Continue to build until cavity preparation is filled to the desired level.
c) Light cure for 20 seconds per surface and continue with preparation.
|
STORAGE: Store at room temperature (20°C/68°F - 25°C/77°F). See individual component labels for specific expiration dates.
PRECAUTIONS:Unpolymerized resins may cause skin sensitization in susceptible persons. In case of contact with the skin, wash thoroughly with soap and water.
WARRANTY:BISCO, Inc. recognizes its responsibility to replace products if proven to be defective. BISCO, Inc. does not accept liability for any damages or loss, either direct or consequential, stemming from the use of or inability to use the products as described. Before using, it is the responsibility of the user to determine the suitability of the product for its intended use. The user assumes all risk and liability in connection therewith.
CAUTION:U.S. Federal law restricts this device to sale by or on the order of a dental professional.
* BIS-CORE is a trademark of Bisco, Inc.
* ALL-BOND 2, ALL-BOND 3, ONE-STEP, ALL-BOND SE and UNI-ETCH are registered trademark of Bisco, Inc.
Bisco, Inc.
1100 W. Irving Park Rd.
Schaumburg, IL 60193
U.S.A.
1-800-BIS-DENT
847-534-6000
www.bisco.com
CE ADMINISTRATOR
Bisico France -
Mr. Fred Picavet
L'Opera- BP. 60
13680 Lançon De Provence
France
Phone: 33-490-42-9292
Fax: 33-490-42-9261
IN-025R4
9/08
|